Keo 2 thành phần PI-3200

CHI TIẾT SẢN PHẨM:

* Keo hệ PVAc, là loại keo sữa 2 thành phần.

* Tỉ lệ: PI-3200 / Hardener = 100 / 10-15

* Công dụng: Ghép ngang, ghép khối các loại gỗ cứng, gỗ dầu.

* Bao bì: Phuy 120Kg, 140Kg, 200Kg; Can 20Kg.

* Xuất xứ: Made in Japan.

Keo Epoxy E44

EPOXY - WSR6101

EPOXY – WSR 6101 is a high performance two component epoxy adhesive. It has
- Superior mechanical strength.
- Exellent bonding strength to wood, concrete, fibreglass, glass, ceramic, marble,
metal, many plastics and other surfaces.
- Thermal resistant.
- Extensively used in marine-timber boat manufacturing and maintenance.
- Seal concrete cracks.
- Water resistance.
- New concept for repair maintenance for industrial and household application.
TECHNICAL DATA
Part A
Epoxy Binder (white Colour)
Part B
Hardener (Amber Colour)

Keo 2 thành phần AD-15

PANATEX AD-15
AQUEOUS VINYL URETHANE ADHESIVE

PANATEX AD-15 is a new type of emulsion system adhesive that can be bonded in the neutral zone of pH. It offers a strong initial bonding strength thus working efficiency is enhanced.

1 - APPLICATION :

{ Production of laminated wood
{ Assembly of furniture and flush bonding.
{ Miscellaneous wood working application in general

2 - GENERAL PROPERTIES:

PROPERTIES
PANATEX AD-15
HARDENER
Cross-linking agent
Appearance
White viscous liquid
Brownish black liquid
Non-volatile matter
41 - 45 %
Effective constituent at more than 98%
Viscosity (at 300C)
85 to 115 poise
2.0 to 4.0 poise
pH
6 to 8


3 - TYPICAL BONDING CONDITIONS :
Adhesive composition
AD-15 / HARDENER
Mixing Ratio
100 / 10÷ 15
Pot Life
50 - 60 minutes
Ambient Temperature
300C
Glue Spread
180 - 250 g/m2
Moisture Content
Lower than 12%
Pressing Time at 300C
30 - 120 minutes

4 - WOOD PREPARATION :

{ Moisture content : Less than 12%
{ Lamination arrangement : control moisture content’s difference of each adjacent laminar less than 5%
{ Thickness Allowance : Within 0.2 mm. This is difference between max. thickness and min. thickness (max. - min. <>

5 - CONDITIONS OF GLUING :

{ Preassembly of laminar : Assemble laminas to fit the size of press machine Mark a line with chalk.
{ Spread : Spread glue by spreader with doctor roller, which is best way to do it. Spread volume : 180 - 250 g/m2 (per one glue line)
Spread by suing spreader, hand - roller, brush, ect. Evenly and quickly on the surface.
Spread volume should be such a amount that even amount of glue is squeezed out from the glue line.
{ Assembly time :
Assembly time is a time from glue spreading to clamping.
Assembly time : 10 minutes at 300C (it depends on temperature)
Among the factors increasing the assembly time are :
a. Type of glue. Liquid glues have longer assembly time than emulsion or dispersion glues.
b. Frequently lower solids increase assembly time.
c. Glue spread. A heavier glue spread increases assembly time.
d. Temperature . A lower temperature increases assembly time.
e. Moisture. Drier woods decrease assembly times.
f. Substrate. Use of high pressure laminate or particle board gives a longer closed assembly time than wood veneers.
g. Ring porous woods such as Oak, Ash, give longer assembly time than Maple or Poplar.
{ Pressing :
Press at fixed pressure rate and hours according to the difference type of glue.
{ Pressure : 5 - 25 kg/cm2
Hard wood :
Specific Gravity more than 0.5 10 - 25 kg/cm2
Soft wood :
Specific Gravity more than 0.5 5 - 10 kg/cm2
Press time : 30 - 120 minutes (at 300C)
It will differ depending on type of glue, wood species, size of laminate and temperature, etc.
{ Aging :
After releasing of pressure, its adhesive has not cured properly yet. So, aging is required.
Before going to next process, need at least 24 hours aging.
To get best bonding performance, 5 days aging under 300C is required.

6 - TEST RESULT :

Cold water soak delamination test : <>

Giới thiệu về Công ty

* Tên Công ty: CÔNG TY TNHH DV - TM ANH ÁNH
* Địa chỉ: Số 1A Đường 9, KP4, An Phú, Quận2, TP. Hồ Chí Minh
* MAIL: anhanhhoakeo@vnn.vn
quangdinhtran@gmail.com
* TEL: 08.37442510
* Fax: 08.37442540
* MST: 0303875307
Công ty chúng tôi tự hào là nhà cung cấp các loại Keo, giấy nhám, màng PE... Phục vụ cho ngành gỗ, trang trí nội thất, thủ công mỹ nghệ, xây dựng... hàng đầu tại Việt Nam. Các sản phẩm của chúng tôi được nhập khẩu Từ Nhật Bản, Thái Lan, Malaysia, Đài Loan, Trung Quốc; những sản phẩm đạt tiêu chuẩn Châu Âu, Nhật Bản...
* Keo trong ngành gỗ:
-Keo sữa một thành phần:
+ Ghép các loại gỗ mềm, chốt mộng, finger joint gỗ,…
+ Chuyên dùng dán Veneer, dán các loại ván nhân tạo, MDF, PB,…
- Keo sữa 2thành phần: Ghép các loại gỗ cứng.
- Keo HOTMELT: Dán cạnh chỉ nhựa Melamin, Veneer gỗ/MDF, Particle Board,…
- EPOXY : Dùng trong xây dựng, xảm trét tầu thuyền, ghép gỗ trên kim loại, bê tông,... xuất xứ Trung Quốc, Malaysia, …
- Keo khô nhanh 502: Dùng để dán gỗ, da, thuỷ tinh, cao su, kim loại, sành sứ,…
- Màng PE: Chuyên cung cấp màng PE Sỉ và Lẻ cho các cá nhân, doanh nghiệp, đại lý.
- Giấy nhám: Hiệu Con ó, YMA, NITTO, JB5... và nhiều hãng nổi tiếng khác.
- Băng keo: Trong, đục, 2 mặt, simili, ...
- Dây đai: Xanh, đỏ, vàng, …
Tất cả các sản phẩm của chúng tôi đều cung cấp với giá cạnh tranh.
Chúng tôi rất mong nhận được sự hợp tác với tất cả các đối tác trên khắp mọi miền tổ quốc.
Liên hệ:
+ Trang Minh Long 0903.732213
+ Trần Quang Đình 0988.438922